KLINGERSIL® C-4243

Characteristic & main applications

Universal gasket material for general industrial applications. Suitable as a gasket material for water, oils, hydrocarbons, liquids and gases at lower pressure and temperatures. Material Based on organic fibres bound with NBR

Material

Based on organic fibres bound with NBR.

 

  1. In area one, the gasket material is normally suitable subject to chemical compatibility.
  2. In area two, the gasket materials may be suitable but a technical evaluation is recommended.
  3. In area three, do not install the gasket without a technical evaluation.

 

 

 

 

Technical Data – Typical values

  • Compressibility ASTM F 36 J : 8% 
  • Recovery ASTM F 36 J min. : 55% 
  • Stress relaxation DIN 52913, 50 MPa, 16 h/175 °C : MPa 24 
  • Klinger cold/hot compression, 50 MPa 
    • thickness decrease at 23°C  : 10% 
    • thickness decrease at 200°C : 25%
  • Tightness acc.DIN 3535/6, mg/s x m : <0,1 
  • Thickness increase ASTM F 146 
    • oil JRM 903, 5 h/150 °C : 5%
    • fuel B, 5 h/20 °C : 7% 
  • Density g/cm3 : 1.75

For International approvals and certification on all materials please contact Klinger/PT Loka Manggala. Certain grades are available with wire or expanded metal reinforcement.